Polymaker Fiberon PA6-CF20 (formerly PolyMide™ PA6-CF) Low-Warp Nylon Filament

Fiberon™ PA6-CF20 is a carbon fiber reinforced (20%) PA6 (Nylon 6) filament. The carbon fiber reinforcement provides significantly improved stiffness, strength and heat resistance with outstanding layer adhesion.

PolyMide™ PA6-CF features Polymaker's Warp-Free™ technology: it enables the production of Nylon-based filaments that can be 3D printed with excellent dimensional stability and near-zero warpage, achieved by fine control of the microstructure and crystallization behavior of the Nylon so the material fully releases internal stress before solidification.

To ensure good heat resistance of your printed part, annealing after printing is recommended.

Density: 1.17 g/cm³

Print Settings

• Printing temperature: 280°C – 300°C
• Build plate temperature: 40°C – 50°C
• Chamber temperature: room temperature
• Printing speed: up to 300 mm/s
• Cooling fan: OFF
• Bed surface: almost any surface with a thin coat of PVA glue or Magigoo PA
• Direct drive retraction: 3 mm / 40 mm/s — indirect drive: 6 mm / 60 mm/s
• Drying (only if the material has absorbed moisture): regular oven 100°C for 10 h, or PolyDryer™ Level 3 for 18 h
• Annealing: 100°C for 16 h

Printing Requirements

• All-metal hotend 280°C+
• Hardened nozzle (carbon fiber is abrasive)
• Filament dryer
• Annealing post printing
• Moisture conditioning after annealing

Official slicer presets: presets.polymaker.com

Fiberon™ PA6-CF20 Technical Data Sheet (V1.1)